CNB-2-CS16
LFP Cathode Sheet (LF0610) Single-sided, 5 pieces/pack
Product Name & Description
LFP Cathode Sheet (LFP0610) is based on Carbon Coated Aluminum Foil coated by Lithium iron phosphate (LF0610) on a single side and can be used as the cathode of Li-Ion battery.
Initial Charge and Discharge Test Conditions:
- Temperature: 25°C
- Charge: First, charge at a constant current of 0.1C to 4.2V, then charge at a constant voltage until the current drops below 0.02C.
- Discharge: Discharge at a constant current of 0.1C to 2.5V.
Rate Performance Test Conditions:
-
Temperature: 25°C
- Charge: First, charge at a constant current of 0.5C to 4.2V, then charge at a constant voltage until the current drops below 0.02C.
- Discharge: Discharge at constant current rates of 0.1C, 0.2C, 0.5C, 1C, 2C, and 3C to 2.5V.
Cycle Test Conditions:
- Temperature: 25°C
- Charge: First, charge at a constant current of 0.5C to 4.2V, then charge at a constant voltage until the current drops below 0.02C.
- Discharge: Discharge at a constant current of 1C to 2.5V.
Specification
| Material |
Lithium iron phosphate |
|
Sheet Size (cm) |
10*10 |
|
Current Collector Thickness (μm) |
14 |
|
Current Collector Areal Density (mg/cm2) |
3.5 |
|
Coating Areal Density (mg/cm2) |
12.3 |
|
Active Material Specific Capacity (mAh:g) |
150mAh/g (2.5-4.2V) |
|
Active Material Ratio (%) |
91.5 |
|
Recommended Compaction Density (g/cc) |
1.5~2.0 |
|
Areal Capacity (mAh/cm2) |
1.69 |
|
Test Conditions |
0.1/0.1C, 2.5-4.2V |
|
Shelf Life |
1 year (vacuum sealed storage), |
|
Instructions For Use |
1.The electrode has been calendered and compacted to a density of 1.8g/cc |
Note: Since the electrodes are single-side-coated, calendering may cause curling issues.