Silicon Carbon 420 Anode Sheet (SC0101) Single-sided, 5 pieces/pack
Product Name & Description
Silicon Carbon 420 Electrode Sheet (SC0101) is based on Copper foil coated by Silicon Carbon 420 Electrode Sheet (SC0101) on a single side and can be used as lithium ion battery.
Initial Charge and Discharge Test Conditions:
- Temperature: 25°C
- Charge: First, charge at a constant current of 0.1C to 2.0V,
- Discharge: Discharge at a constant current of 0.1C/0.09C/0.08C/0.07C/0.06C/0.05C/0.04C/0.03C/0.02C/0.01C stages down to 0.005V.
Rate Performance Test Conditions:
-
Temperature: 25°C
- Charge: First, charge at a constant current at 0.1C/0.2C/0.5C/1C/2C/3C rates up to 2.0V.
- Discharge: Discharge at constant current rates of 1C/0.9C/0.8C/0.7C/0.6C/0.5C/0.4C/0.3C/0.2C/0.1C stages down to 0.005V.
Cycle Test Conditions:
- Temperature: 25°C
- Charge: First, charge at a constant current of 0.5C to 2.0V.
- Discharge: Discharge at a constant current of 1C/0.9C/0.8C/0.7C/0.6C/0.5C/0.4C/0.3C/0.2C/0.1C stages down to 0.005V.
.The electrolyte used corresponding to the performance data is silicon carbon-electrolyte (KLD-Si01).
Specification
| Material |
Silicon carbon 420 |
|
Sheet Size (cm) |
10*10 |
|
Current Collector Thickness (μm) |
8 |
|
Current Collector Areal Density (mg/cm2) |
7.3 |
|
Coating Areal Density (mg/cm2) |
4.45 |
|
Active Material Specific Capacity (mAh:g) |
420mAh/g (0.05-2.0V) |
|
Active Material Ratio (%) |
95.0 |
|
Recommended Compaction Density (g/cc) |
1.3~1.55 |
|
Test Conditions |
0.1/0.1C, 0.05-2.0V |
|
Shelf Life |
1 year (vacuum sealed storage), |
|
Instructions For Use |
1. The electrode calendering, needs to be calendered according to the recommended compaction density. |
Note: Since the electrodes are single-side-coated, calendering may cause curling issues.