CNB-2-CS20
Sodium Nickel Iron Manganese Oxide Cathode Sheet (NT0103) Single-sided, 5 pieces/pack
Product Name & Description
Sodium Nickel Iron Manganese Oxide Cathode Sheet (NT0103) is based on Aluminum foil coated by Sodium Nickel Iron Manganese Oxide (NT0103) on a single side and can be used as the cathode of sodium ion battery.
Initial Charge and Discharge Test Conditions:
- Temperature: 25°C
- Charge: First, charge at a constant current of 0.1C to 4.0V, then charge at a constant voltage until the current drops below 0.02C.
- Discharge: Discharge at a constant current of 0.1C to 2.0V.
Rate Performance Test Conditions:
-
Temperature: 25°C
- Charge: First, charge at a constant current of 0.5C to 4.0V, then charge at a constant voltage until the current drops below 0.02C.
- Discharge: Discharge at constant current rates of 0.1C, 0.2C, 0.5C, 1C, 2C, and 3C to 2.0V.
Cycle Test Conditions:
- Temperature: 25°C
- Charge: First, charge at a constant current of 0.5C to 4.0V, then charge at a constant voltage until the current drops below 0.02C.
- Discharge: Discharge at a constant current of 1C to 2.0V.
The electrolyte used for the performance data is: sodium electrolyte MA-EN-EL-0P0616 1.0M NaClO4 in EC: DEC=1:1 Vol% with 5.0% FEC
Specification
| Material |
Sodium Nickel Iron Manganese Oxide |
|
Sheet Size (cm) |
10*10 |
|
Current Collector Thickness (μm) |
12 |
|
Current Collector Areal Density (mg/cm2) |
3.30 |
|
Coating Areal Density (mg/cm2) |
8.0 |
|
Active Material Specific Capacity (mAh:g) |
120mAh/g |
|
Active Material Ratio (%) |
94.0 |
|
Recommended Compaction Density (g/cc) |
2.0~2.5 |
|
Test Conditions |
0.1/0.1C, 2.0-4.0V |
|
Shelf Life |
1/2 year (vacuum sealed storage), |
|
Instructions For Use |
1. The electrode calendering, needs to be calendered according to the recommended compaction density. |
Note: Since the electrodes are single-side-coated, calendering may cause curling issues.